Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- CASE Ingredients Features
- Specific Features
- Polymer
- Solvent-based
Applications & Uses
- Markets
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Coating Type
- Applications
- Release Coatings
- Tapes & Electronics
- Application Details
DEHESIVE® 953 may be used for coating of PE-laminated paper and papers. It is particularly recommended for coating of thermoplastic films such as PE and PP.
Processing
Generally DEHESIVE® 953 is diluted to give a formulation with an active substance content of about 5 %. However, depending on the substrate and coater system, DEHESIVE® 953 may be used with lower or higher active substance contents. Special care must be taken to select a high quality solvent that will not poison the Pt-catalyst. Common poisons are organo-tin compounds, sulfur compounds (a common source are rolls that have been vulcanized with sulfur), amines, acid amides, zinc stearate and phosphites. The quality of the coating compound can be ensured by using clean vessels of stainless steel, enamel, plastic or glass to prepare the batch. Batches of coating compound must be prepared in the order given below.
- First pour DEHESIVE® 953 in several portions and stir slowly until the mixture is homogeneous
- Add solvent and stir slowly until the mixture is homogeneous
- Add CRA® release modifier in case CRA® is used and stir slowly until the mixture is homogeneous
- Thoroughly stir in Crosslinker to this mixture 5. Slowly stir in catalyst
Local over-concentrations must be avoided. Suitable solvents are aliphatic and aromatic hydrocarbons (e.g. toluene, white spirit), esters and ketones. The cure speed depends on the formulation (e.g. the amount of catalyst), type of substrate, quality of solvent, the chosen temperature and the effectiveness of the oven. Laboratory trials are recommended prior to using the material in production in order to verify that the vulcanization performance suits the intended application.
Properties
- Typical Properties
- Properties
- Fast curing
- Low release at low peel speeds
- Good release stability
- Good bath life
- Suitable for coating PP and PE films and PE-coated paper
| Value | Units | Test Method / Conditions | |
| Density | 0.92 | g/cm³ | — |
| Dynamic Viscosity (at 25°C) | approx. 1200 | mPa·s | — |
| Flash Point | 4 | °C | DIN 51755 |
| Ignition Temperature | min. 500 | °C | DIN 51794 |
| Solid Content | approx. 55 | % | — |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Packaging & Availability
- Country Availability
- Regional Availability