Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Method
- Applications
- ELASTOSIL - Ready-to-Use Construction Sealants
- Sealants
- Silicone Sealants
- Application Details
Application Fields
- Sealing of connecting and expansion joints in the construction industry
- Glass sealing
- Sealing of joints in sanitary areas like e.g. Bathrooms and kitchens
- Sealing of joints between glazing and supporting structure (frames, transoms, mullions)
Processing
- The substrate areas that will be in contact with the sealant must be clean, dry and free of all loose material, dust, dirt, rust, oil and other contaminants. Non-porous substrates should be cleaned with a solvent and a clean, lint-free, cotton cloth. Remove residual solvent before it evaporates with a fresh clean, dry cloth.
- It is the responsibility of the user to test the compatibility of the sealant with the adjoining materials. Incompatible substances like coating materials (paints, varnishes and glazes) or organic plasticizer containing rubbers (EPDM, butyl and neoprene) can lead to discoloration or other impairments like loss of adhesion of the sealant.
- Materials in direct contact with the applied sealant like cleaning agents and materials in indirect contact like gaseous emissions can damage the sealant in its function or change its appearance.
- Even a longer period of time in the darkness white joints may show a slight yellowing.
- Because of the multitude of these materials WACKER cannot make a general statement to the compatibility or adhesion of materials with the sealant.
- In case of doubt the user shall conduct appropriate preliminary tests. The time until complete curing may be extended at lower temperature, lower humidity, increasing film thickness or by low volume of air exchange.
Adhesion
ELASTOSIL® 7100 P exhibits excellent primerless adhesion to most material used for sanitary application, e.g. glass, tiles, ceramics, enamel, glazed tiles and clinker on varnished or painted wood Users must carry out their own tests due to the great variety of substances. The adhesion can be improved in many cases by pretreatment of the substrates with a primer.
Properties
- Cured Properties
- Uncured Properties
- Properties
- Suitable for use in sanitary areas
- 100% silicone
- Long shelf life
- Primerless adhesion to most materials
- Non-corrosive to metals
- Suitable for alkaline substrates such as concrete, mortar, fibrous cement
- Almost odorless
- Non-sag
- Ready gunnability at low (+5 °C) and high (+40 °C) temperatures
- Rapid crosslinking: quickly becomes tack-free
- Flexible at low (-40 °C) and high temperatures (+180 °C)
- Excellent weatherability
- Excellent processing characteristics for professional use
| Value | Units | Test Method / Conditions | |
| Elongation (at break) | min. 300 | % | ISO 8339-A |
| Modulus (at 100 % elongation) | 0.38 | N/mm² | ISO 8339-A |
| Movement Capability | 25 | % | ISO 11600 |
| Shore Hardness A | 24 | — | ISO 868 |
| Tear Strength | 4.6 | — | ISO 34 – C |
| Tensile Strength | 0.7 | N/mm² | ISO 8339-A |
| Value | Units | Test Method / Conditions | |
| Consistency (at 23°C) | Non-sag | — | ISO 7390, Profile U 20 |
| Curing rate | approx. 3 | mm/day | — |
| Density (at 23°C) | 1.03 | g/cm³ | ISO 1183-1 A |
| Extrusion Mass Flow Rate (at 6 bar, 23°C) | 200 | g/min | — |
| Skin Formating Time (at 23°C, 50% r.h) | 25 | minutes | — |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Quality Standards
- Restrictions in Use
- ELASTOSIL® 7100 P must not be used as a secondary sealant in insulating glass units.
- ELASTOSIL® 7100 P must not be used for structural glazing bonding.
- ELASTOSIL® 7100 P is not suitable for use on natural stones, such as marble, granite, quartzite, as it can cause staining.
- ELASTOSIL® 7100 P is not suitable for the construction of aquaria.
- ELASTOSIL® 7100 P is not suitable for food contact applications.
- ELASTOSIL® 7100 P is not recommended for application in permanently wet areas where the joint is strongly or permanently exposed to water, e.g. in swimming pools, please contact our technical service.
- ELASTOSIL® 7100 P is not suitable for use as a mirror adhesive.
Safety & Health
- Safety Note
- During vulcanization ethanol is released. These vapors should not be inhaled for long periods or in high concentration. Hence, good ventilation of the work place is necessary.
- Should unvulcanized RTV-1 silicone rubber come into contact with eyes or mucous membranes, the affected area must be rinsed thoroughly with water as irritation will otherwise be caused. Cured silicone rubber, however, can be handled without any risk to health. Keep away from children.
Packaging & Availability
- Country Availability
- Regional Availability