Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Special Features
- Addition-curing
- BfR compliant
- FDA compliant
- Low viscosity
- No shrinkage
- Two-component
Applications & Uses
- Markets
- Cure Method
- Plastics & Elastomers End Uses
- Application Details
- Due to the outstanding resistance to casting resins as well as the superior mechanical properties, ELASTOSIL M 4601 A/B is especially suitable for all molds of models with extensive undercuts that are to be reproduced in casting resins.
- As a low-Shore addition-curing RTV-2 silicone rubber that cures without undergoing dimensional shrinkage, ELASTOSIL® M 4601 A/B is also extremely suitable for casting all other common reproduction materials, particularly if absolutely accurate copies of models with pronounced undercuts are required.
Processing
- The platinum catalyst is in component B.
- A and B components may only be used together if they have the same batch number.
- Applications
- Making shrink-free molds with excellent reproduction accuracy.
- Automotive molding
- Reproduction Molding
Properties
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Very good flow
- Low viscosity
- Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat.
- Low Shore A hardness (approx. 28)
- High tear strength
- Excellent long-term stability of the mechanical properties of the cured rubber.
- Outstanding resistance to common casting resins particularly polyurethane.
- Note
Cured properties are vulcanized after 24 h at 23 °C.
Value | Units | Test Method / Conditions | |
Curing Time (tack-free) | 12 | hours | — |
Dynamic Viscosity (at 23°C) | 10000 | mPa·s | ISO 3219 |
Mix Ratio (A:B) | 9:1 | parts by weight | — |
Processing Time (up to 60000 mPa.s) | 90 | minutes | — |
Value | Units | Test Method / Conditions | |
Density (in water, at 23°C) | 1.13 | g/cm³ | ISO 2781 |
Elongation (at break) | 700 | % | ISO 37 |
Linear Shrinkage | max. 0.1 | % | — |
Shore Hardness A | 28 | — | ISO 868 |
Tear Strength | min. 30 | N/mm | ASTM D 624 B |
Tensile Strength | 6.5 | N/mm² | ISO 37 |
Value | Units | Test Method / Conditions | |
Density (at 23°C, Componenet A) | 1.14 | g/cm³ | — |
Density (at 23°C, Componenet B) | 1.01 | g/cm³ | — |
Dynamic Viscosity (Component A, at 23°C, after stirring) | 15000 | mPa·s | ISO 3219 |
Dynamic Viscosity (Component B, at 23°C, after stirring) | 800 | mPa·s | ISO 3219 |