| Brookfield Viscosity (Solid Content 40% in styrene, 20 rpm, PML 002, at 23°C) | 300 | mPa.s | Brookfield Viscometer |
| Brookfield Viscosity (Solid Content in styrene 50%, 20 rpm, PML 002, at 23°C) | 1200 | mPa.s | Brookfield Viscometer |
| Bulk Density | approx. 700 | kg/m³ | DIN 53466 |
| Brookfield Viscosity (Solid Content in styrene 60%, 20 rpm, PML 002, at 23°C) | 9200 | mPa.s | Brookfield Viscometer |
| Density (of the polymer) | approx. 1.20 | g/cm³ | DIN EN ISO 1183 /1-3 |
| Melt Viscosity (100% Polymer, at 100°C) | approx. 2600 | Pa.s | Bohlin high temperature viscosimeter |
| Glass Transition Temperature | approx. 37 | °C | DSC (DIN 53765 / ISO 11357-5) |
| Melt Viscosity (100% Polymer, at 120°C) | approx. 210 | Pa.s | Bohlin high temperature viscosimeter |
| K-Value | approx. 25 | - | DIN 53726 |
| Melt Viscosity (100% Polymer, at 140°C) | approx. 50 | Pa.s | Bohlin high temperature viscosimeter |
| Molecular Weight (Mw) | approx. 30000 | g/mol | SEC, PS-Standard |
| Softening Point | approx. 101 | °C | ASTM D 3104 |
| Volatile Content | max. 0.5 | wt % | Specific method |