- ELASTOSIL LR 6360 F is a multi-purpose liquid silicone rubber with low viscosity to produce textile coatings with a stiff hand and a dry surface. Due to the high additive tolerance the viscosity of mixtures with adhesion promotors will increase only moderately.
- Therefore, ELASTOSIL® LR 6360 F is especially well suited for textile coatings with demanding adhesion requirements. The hardness and elasticity of the coating can ve varied in combination with ELASTOSIL® LR 6320 F.
- The components of ELASTOSIL® LR 6360 F are in compliance with the positive lists of the Recommendation XV. Silicones of the BfR and FDA 21 CFR §175.300 and 177.2600. However, for compliance of the finished article with the before mentioned regulations the product has to be appropriately cured and given limitations on extractable and volatile substances have to be met.
Processing
- ELASTOSIL® LR 6360 F is processed by thorough incorporation of a crosslinker.
- Recommended ratio is 100 parts of ELASTOSIL® LR 6360 F plus
- 4.5 parts of CROSSLINKER W
- Recommended curing conditions: 3 min at 150°C or 1 min at 180°C
- Adhesion of ELASTOSIL® LR 6360 F depends on substrate and can be varied by crosslinker type/amount and additives (e.g. CATALYST C05 or adhesion promoters). Preliminary testing should be carried out to determine optimum formulation and cure conditions.
Properties
- Typical Properties
- Cured Properties
- Uncured Properties
- Properties
- Low viscosity material for textile coating applications
- High additive tolerance for complicated adhesion problems
- Hard elastic film in combination with CROSSLINKER W
- Variable hardness in combination with ELASTOSIL® LR 6320 F
- Note
Mixture 100 parts LR 6360 F + CROSSLINKER W, 5 min, 165 °C for cured properties.
| Value | Units | Test Method / Conditions | |
| Pot Life (at 23°C) | 3 | Days | — |
| Value | Units | Test Method / Conditions | |
| Density | 1.07 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 150 | % | ISO 37 Type 1 |
| Shore Hardness A | 60 | — | DIN ISO 48-4 |
| Tear Strength | 6.1 | N/mm | ASTM D 624 B |
| Tensile Strength | 5 | N/mm² | ISO 37 Type 1 |
| Value | Units | Test Method / Conditions | |
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 38000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 28000 | mPa·s | DIN EN ISO 3219 |
Packaging & Availability
- Country Availability
- Regional Availability
- Packaging Information
This product is available in 25 kg pails and 200 kg drums.
Storage & Handling
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.