- Materials Features
- Special Features
- Addition-curing
- Excellent mechanical properties
- No shrinkage
- Strong oil bleeding
- Two-component
Applications & Uses
- Markets
- Compatible Polymers & Resins
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application Details
High-performance silicone mold-making compound which is particularly suitable for reproducing models with undercuts in polyurethane or epoxy resins.
Processing
Important note:
- The platinum catalyst is in component B.
- A and B components may only be used together if they have the same batch number.
- Applications
- Prototype Molding
- Vacuum casting for rapid prototyping.
Properties
- Color
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Very good flow
- Excellent mold release, usually no further release agent required
- Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat.
- Medium shore A hardness
- Good transparency of the cured rubber
- High tear strength
- Outstanding resistance to casting resins, particularly polyurethanes and epoxies, for long service life of the molds.
- Strong oil-bleeding
- Note
Cured properties are vulcanized after 24 h at 23 °C.
Value | Units | Test Method / Conditions | |
Curing Time (A+B, tack-free) | 12 | hours | — |
Dynamic Viscosity (A+B, at 23°C) | 35000 | mPa·s | ISO 3219 |
Mix Ratio (A:B) | 10:1 | parts by weight | — |
Pot Life (A+B, at 23°C, up to 150000 mPa.s) | 80 | minutes | — |
Value | Units | Test Method / Conditions | |
Density (in water, at 23°C) | 1.06 | g/cm³ | ISO 2781 |
Elongation (at break) | 330 | % | ISO 37 |
Linear Shrinkage | max. 0.1 | % | — |
Shore Hardness A | 40 | — | ISO 868 |
Tear Strength | min. 28 | N/mm | ASTM D 624 B |
Tensile Strength | 5 | N/mm² | ISO 37 |
Value | Units | Test Method / Conditions | |
Density (at 23°C, Componenet A) | 1.08 | g/cm³ | — |
Density (at 23°C, Componenet B) | 0.97 | g/cm³ | — |
Dynamic Viscosity (Component A, at 23°C, after stirring) | 50000 | mPa·s | ISO 3219 |
Dynamic Viscosity (Component B, at 23°C, after stirring) | 3500 | mPa·s | ISO 3219 |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety Note
Components of the addition-curing grade ELASTOSIL® M 4645 A/B contain only constituents that over many years have proved to be neither toxic nor aggressive. Special handling precautions are therefore not required, i.e., only the general industrial hygiene regulations apply.
Packaging & Availability
- Country Availability
- Regional Availability