Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Special Features
- Non-slump
- Thixotropic
- Tin-free catalysis
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Method
- Applications
- Automotive Electronics
- Automotive, Aerospace & Railway
- Formed-In-Place-Gaskets (Wet Type)
- Heating, Ventilation, Air Conditioning (HVAC)
- Household Applications
- Luminaires
- Measurement & Control, Sensor Technology
- Small Appliances
- White Goods
- Application Details
During vulcanization of ELASTOSIL® N9111 GRAY, a total of 3% by weight of alcohol is split off. These vapors should not be inhaled for long periods or in high concentration. Work areas should therefore be well ventilated.
Properties
- Color
- Typical Properties
- Cured Properties
- Uncured Properties
- Properties
- Excellent adhesion to many substrates
- No inhibition effect to platinum-catalyzed grades.
- No use of organotin catalysts
- Medium hardness shore A.
- Note
Curing Conditions: 14 days at 23°C and 50% rel. humidity, 2 mm sheet, no post-curing.
| Value | Units | Test Method / Conditions | |
| Recommended Service Temperature | -45 to +180 | °C | — |
| Value | Units | Test Method / Conditions | |
| Density (in water, at 23°C) | 1.33 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Type 3, 23°C, 2mm) | 500 | % | ISO 37 |
| Shore Hardness A | 30 | — | DIN ISO 48-4 |
| Tensile Strength (Type 3, at 23°C, 2mm) | 2.2 | N/mm² | ISO 37 |
| Value | Units | Test Method / Conditions | |
| Curing Speed (at 23°C, 50% r.h) | 2 | mm/day | — |
| Density | 1.3 | g/cm³ | DIN EN ISO 1183-1 A |
| Dynamic Viscosity (at 25°C, Shear rate 0.5 s⁻¹) | 1000000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (at 25°C, Shear rate 25 s⁻¹) | 100000 | mPa·s | DIN EN ISO 3219 |
| Skin Formating Time | 20 - 40 | minutes | Internal method |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety Note
During vulcanization of ELASTOSIL® N9111 GREY, a total of 3% by weight of alcohol is split off. These vapors should not be inhaled for long periods or in high concentration. Work areas should therefore be well ventilated.