Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Method
- Applications
- Automotive Electronics
- DO NOT USE Potting & Encapsulation with Tough Gels
- Electrics & Electronics
- Measurement & Control, Sensor Technology
- Application Details
Only components A and B with the same lot number may be processed together.
Properties
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Two-part, 1 : 1 mixing ratio
- Very low hardness
- Low risk of inhibition
- Rapid heat cure
- Primerless adhesion
- Note
Cured Properties: Cured for 30 min at 150°C.
Value | Units | Test Method / Conditions | |
Dynamic Viscosity (A+B, at 23°C, of mix) | 1000 | mPa·s | ISO 3219 |
Mix Ratio (A:B) | 1:1 | parts by weight | — |
Platinum Catalyst in Component (A+B) | Component A | — | — |
Pot Life (A+B, at 23°C, up to 100000 mPa.s) | min. 4 | hours | — |
Value | Units | Test Method / Conditions | |
Curing Time (at 120°C, 1 mm thickness) | 10 | min | — |
Curing Time (at 150°C, 1 mm thickness) | 5 | min | — |
Curing Time (at 80°C, 1 mm thickness) | 60 | min | — |
Density (at 23°C) | 0.97 | g/cm³ | — |
Modulus (at 100 % elongation) | 0.05 | N/mm² | ISO 37 |
Shore Hardness 00 | 37 | — | ASTM D 2240 |
Volume Resistivity | 10¹⁵ | Ohm-cm | IEC 60093 |
Value | Units | Test Method / Conditions | |
Density (at 23°C, Componenet A) | 0.97 | g/cm³ | — |
Density (at 23°C, Componenet B) | 0.97 | g/cm³ | — |
Dynamic Viscosity (Component A, at 23°C) | 1000 | mPa·s | ISO 3219 |
Dynamic Viscosity (Component B, at 23°C) | 1000 | mPa·s | ISO 3219 |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety Notes
According to the latest findings, addition-curing silicone rubber ELASTOSIL® RT 745 "S" A/B contains neither toxic nor aggressive substances which would require special handling precautions. General industrial hygiene regulations should be observed.