Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Specific Features
- MIL-A 46106 grade
- Non-slump
- One-component
- Technical grade
- Thixotropic
Applications & Uses
- Applications
- Application Area
- Cure Method
- Applications
- Appliances Industry
- Luminaires
- Small Appliances
- Application Details
ELASTOSIL® E47 TRANSPARENT is a multipurpose grade for sealing and bonding. It is in particular suited as adhesive for cured silicone such as profiles, prosthetics inliners etc.
Processing
ELASTOSIL® E47 TRANSPARENT shows good primerless adhesion to many substrates. We recommend running preliminary tests to optimize conditions for the particular application.
Properties
- Color
- Physical Form
- Cured Properties
- Uncured Properties
- Properties
- Non-sag, soft paste
- High extrusion rate
- Outstanding adhesion to cured silicone rubber
- Note
Curing Conditions: 14 days at 23°C and 50 % relative humidity, 2 mm sheet, no post-curing.
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.07 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Type 3, 23°C, 2mm) | 450 | % | ISO 37 Type 1 |
| Shore Hardness A | 37 | — | DIN ISO 48-4 |
| Tensile Strength (Type 3, at 23°C, 2mm) | 4.5 | N/mm² | ISO 37 Type 1 |
| Value | Units | Test Method / Conditions | |
| Density | 1.12 | g/cm³ | DIN EN ISO 1183-1 A |
| Dynamic Viscosity (at 25°C, Shear rate 0.5 s⁻¹) | 600000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (at 25°C, Shear rate 25 s⁻¹) | 80000 | mPa·s | DIN EN ISO 3219 |
| Extrusion Mass Flow Rate (3.1 mm nozzle, 0.21 N/mm² pressure) | 10 | g/10s | Internal method |
| Skin Formating Time (at 23°C, 50% r.h) | 10 | minutes | — |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Quality Standards
- Compliance
Meets the physical requirements of MIL-A-46106, Group I, Type I and Group II, Type I.
Safety & Health
- Safety Notes
During vulcanization of ELASTOSIL® E47 TRANSPARENT, a total of 3% by weight of acetic acid is split off. These vapors should not be inhaled for long periods or in high concentration. Work areas should therefore be well ventilated. Contact of unvulcanized silicone rubber with eyes and mucous membranes must be avoided as this would cause irritation. However if it does happen, rinse the affected area thoroughly with water.
Packaging & Availability
- Country Availability
- Regional Availability