ELASTOSIL® LR 3072 series are particularly suitable for the economical production of large series of overmolded parts (thermoplastic/elastomer), even in a comolding process (shuttle mold) under standard conditions, without any special treatment of the mold surface. They are increasingly being used to produce cable and connector seals for the automotive industry. As an oil film forms, seals can be fitted easily and fully-automatically, even when tolerances are narrow. Parts made from ELASTOSIL® LR 3072 can generally be used for technical applications without post-curing, but do not comply with regulations concerning use in the pharmaceutical and food industry.
Processing
The A and B components are delivered ready to use in 20 kg pail and 200 kg drum kits. With adequate metering equipment, they can be pumped directly from the original containers into the injection molding machine and mixed by a static mixer. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days.
Note : Start-up of new molds should be supported by use of ELASTOSIL® AUX Mold Release Agent 32.
Properties
- Color
- Physical Form
- Cured Properties
- Uncured Properties
- Properties
ELASTOSIL® LR 3072 series are primerless, selfbonding grades that adhere to various plastic substrates (e. g. PA, PBT) and metals, but not in the mold. The bonding is improved by a subsequent heat treatment process (e.g. one hour at 100°C) or by a longer storing at room temperature. Because of the individual surface properties adhesion to the substrate must be tested before production.
- Note
Cure conditions : 5 min / 165°C in press.
| Value | Units | Test Method / Conditions | |
| Compression Set (at 22 hours, 125°C) | 21 | % | DIN ISO 815-1 type B method A |
| Compression Set (at 22 hours, 150°C) | 35 | % | DIN ISO 815-1 type B method A |
| Compression Set (at 22 hours, 175°C) | 48 | % | DIN ISO 815-1 type B method A |
| Density | 1.12 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 620 | % | ISO 37 Type 1 |
| Rebound Resilience | 50 | % | ISO 4662 |
| Shore Hardness A | 40 | — | DIN ISO 48-4 |
| Tear Strength | 21 | N/mm | ASTM D 624 B |
| Tensile Strength | 8.8 | N/mm² | ISO 37 Type 1 |
| Value | Units | Test Method / Conditions | |
| Dynamic Viscosity (Shear rate 1 s⁻¹) | 1600000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (Shear rate 10 s⁻¹) | 330000 | mPa·s | DIN EN ISO 3219 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Packaging Information
This product is available in 20 kg pail and 200 kg drum kits.
Storage & Handling
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.