Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Special Features
- Flame retardant
- Low viscosity
- One-component
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Method
- Applications
- Automotive Electronics
- Formed-In-Place-Gaskets (Wet Type)
- Luminaires
- Application Details
Multipurpose grade for sealing and bonding such as FIPG-applications for e.g. automotive headlamps.
Processing
- ELASTOSIL® N 2034 is a ready-to-use, acid- and sovent-free, non-corrosive RTV-1 (room temperature vulcanizing, onecomponent) silicone rubber suitable for many applications. Excellent adhesion to plastics and metals in combination with a high elasticity and durability open up a wide range of potential uses for ELASTOSIL® N 2034.
- The consistency of the uncured material allows a high application rate and makes it a good choice not only for dispensing from a caulking gun but also for automatic dispensing. The fully cured rubber can withstand expansion-compression cycles for many years and is therefore especially well suited for joining materials with different coefficients of thermal expansion.
- The vulcanized silicone rubber permanently remains elastic over a wide temperature range from -50°C to +180°C (-58 °F to +356 °F). If removing of silicone rubber from machines or dispensing equipment is necessary, white spirit is recommended as a solvent. However, cleaning should take place before the rubber is fully cured.
- Afterwards only the use of mechanical forces in combination with a swelling solvent or the use of high temperatures of approximately 100°C will help to remove sealant residues.
Properties
- Flame Rating
- Typical Properties
- Cured Properties
- Uncured Properties
- Properties
- Flame retardant (meets UL 94 V-0)
- Self-leveling
- Note
Curing Conditions: 14 days at 23°C and 50% rel. humidity, 2 mm sheet, no post-curing
| Value | Units | Test Method / Conditions | |
| Recommended Service Temperature | -45 to +180 | °C | — |
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.16 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 200 | % | ISO 37 |
| Shore Hardness A | 35 | — | DIN ISO 48-4 |
| Tensile Strength (Type 3, at 23°C, 2mm) | 2 | N/mm² | ISO 37 |
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.15 | g/cm³ | DIN EN ISO 2811-1 |
| Dynamic Viscosity (at 25°C, Shear rate 0.5 s⁻¹) | 30000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (at 25°C, Shear rate 25 s⁻¹) | 12500 | mPa·s | DIN EN ISO 3219 |
| Skin Formating Time (at 23°C, 59% r.h) | 20 | minutes | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety Note
ELASTOSIL N 2034 releases during cure a total 3% alcohol. These vapors should not be inhaled for long periods or in high concentrations. Hence good ventilation of the works place is necessary.
Packaging & Availability
- Country Availability
- Regional Availability