Knowde Enhanced TDS
Identification & Functionality
- Carrier
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Specific Features
- Flexible at low (-40°C) and high temperatures (+180°C)
- Flowable
- Low viscosity
- Solvent-based
Applications & Uses
- Applications
- Application Area
- Cure Method
- Applications
- DO NOT USE Small Appliances
- Heating, Ventilation, Air Conditioning (HVAC)
- Small Appliances
- Application Details
Multipurpose sealant and coating material.
Processing
- ELASTOSIL® A07 TRANSLUCENT is a free flowable, solvent-based RTV-1 silicone dispersion. It cures at room temperature reaction with air humidity to a flexible silicone coating. During cure it splits off an organic amine. It can be applied by dipping, spraying, brushing or coating.
- Thinner coatings can be obtained by addition of solvents (e.g. toluene, white spirit), thicker coatings can be realized by multiple step coating. The product contains about 25% of solvent (b.w.) therefore suitable equipment has to be used and precaution measures due to the solvent vapors have to be taken.
- ELASTOSIL® A07 TRANSLUCENT is a one-part room temperature curing coating therefore the curing rate depend atmospheric humidity.
- The curing rate can be accelerate on exposure to carbon dioxide concentration above 1% p.b.v. Uncured or partially cured silicone can be removed by help of organic solvents such as alipatic or aromatic hydrocarboncleaning should take place before the rubber is fully cured.
- Once completely cured, only mechanical removal supported by prior solvent swell is possible. In thin films, Wacker Silicone Remover S8 is suited as well.
Properties
- Color
- Cured Properties
- Uncured Properties
- Properties
- Ready-to-use, one-component system
- Low module
- Excellent primerless adhesion to many substrates
- No use of organotin catalysts
- Note
Cured Conditions: 2 mm, 14 days storage at 20 °C, 50 % RH.
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.02 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 300 | % | ISO 37 Type 1 |
| Shore Hardness A | 20 | — | DIN ISO 48-4 |
| Tensile Strength | 1.5 | N/mm² | ISO 37 Type 1 |
| Value | Units | Test Method / Conditions | |
| Curing Time (at 23°C, 50 %r.h) | 12 | hour/mm | — |
| Density | 0.98 | g/cm³ | DIN 51757 |
| Dynamic Viscosity (at 23°C, Brookfield, spindle 3, 5 rpm) | 8000 | mPa·s | DIN EN ISO 2555 |
| Skin Formating Time (at 23°C, 50% r.h) | 5 | minutes | — |
| Solvent Content (Toluene) | 25 | % | — |