Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Specific Features
- Food-contact
- Fast curing
- High tear-resistant
- Reduced volatile content
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
- Baby Care
- Dairy Applications
- General Automotive Parts
- Household Applications
- Molded Parts
- Molded Seals (LSR)
- Application Details
These grades are particularly suitable for the economical production of large series of injection-molded articles. Parts made from ELASTOSIL® LR 3040/40 A/B can be used for technical applications. These articles are also suitable for use in conjunction with foodstuffs. Postcured parts can be used for food contact applications and are suitable for use under the Recommendation "XV. Silicones" of the BfR and FDA § 177.2600 under observance of any given limitations on extractable and volatile substances.
Processing
The A and B components are delivered ready to use in 20 kg pail and 200 kg drum kits. With adequate metering equipment, they can be pumped directly from the original containers into the injection molding machine and mixed by a static mixer. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least one day. The vulcanization (t90 value) is 20 to 40% shorter than of products in the ELASTOSIL® LR 3043 series. This consequently leads to a decrease in cycle times and thus to cost savings, depending on the injection-molded articles.
Properties
- Physical Form
- Cured Properties
- Uncured Properties
- Properties
Narrow Shore hardness range from 38 to 44 Shore A (41 ± 3 Shore A). This product can be used within a temperature range of - 55°C to + 210°C. The addition of heat stabilizers at service temperatures of more than 180°C is recommended.
- Note
Cure conditions : 5 min / 165°C in press, post-cured 4 h / 200°C.
Value | Units | Test Method / Conditions | |
Compression Set (at 22 hours, 175°C) | 11 | % | DIN ISO 815-1 type B method A |
Density | 1.12 | g/cm³ | DIN EN ISO 1183-1 A |
Elongation (at break) | 600 | % | ISO 37 Type 1 |
Rebound Resilience | 58 | % | ISO 4662 |
Shore Hardness A | 40 | — | DIN ISO 48-4 |
Tear Strength | 11 | N/mm | DIN ISO 34-1 A |
Tear Strength | 36 | N/mm | ASTM D 624 B |
Tensile Strength | 9 | N/mm² | ISO 37 Type 1 |
Value | Units | Test Method / Conditions | |
Dynamic Viscosity (Shear rate 1 s⁻¹) | 870000 | mPa·s | DIN EN ISO 3219 |
Dynamic Viscosity (Shear rate 10 s⁻¹) | 380000 | mPa·s | DIN EN ISO 3219 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Packaging Information
This product is available in 20 kg pail and 200 kg drum kits.
Storage & Handling
- Storage Information
Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.