Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Special Features
- Addition Curing
- BfR compliant
- Excellent mechanical properties
- FDA compliant
- Flowable
- Food-contact
- Low viscosity
- No chemical shrinkage
- Resistance against casting resins
- Resistance against concrete
- Two-component
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Application Details
- Due to its outstanding resistance to concrete and superior mechanical properties, ELASTOSIL® M 4630 A/B is ideal for use in molds for making concrete reproductions of models with deep undercuts.
- As a low-shore, addition-curing RTV-2 silicone rubber, which cures without dimensional shrinkage, ELASTOSIL® M 4630 A/B is also extremely suitable for casting all other common reproduction materials, especially casting resins where absolutely accurate copies of models with pronounced undercuts are required.
Processing
Important note:
- The platinum catalyst is contained in component B.
- Only components A and B with the same lot number may be processed together.
- Applications
Construction Molding
Properties
- Color
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Very good flow
- ;Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat.
- Low shore a hardness (approx. 28)
- High tear strength
- Excellent long-term stability of the mechanical properties of the vulcanizate.
- Outstanding resistance to concrete
| Value | Units | Test Method / Conditions | |
| Curing Time (tack-free) | 12 | hours | — |
| Dynamic Viscosity (at 23°C) | 10000 | mPa·s | ISO 3219 |
| Mix Ratio (A:B) | 10:1 | parts by weight | — |
| Pot Life (at 23°C, 60000 mPa·s) | 90 | minutes | — |
| Value | Units | Test Method / Conditions | |
| Density (in water, at 23°C) | 1.13 | g/cm³ | ISO 2781 |
| Elongation (at break) | 700 | % | ISO 37 |
| Linear Shrinkage | max. 0.1 | % | — |
| Shore Hardness A | 28 | — | ISO 868 |
| Tear Strength | min. 30 | N/mm | ASTM D 624 B |
| Tensile Strength | 6.5 | N/mm² | ISO 37 |
| Value | Units | Test Method / Conditions | |
| Density (at 23°C, Componenet A) | 1.14 | g/cm³ | — |
| Density (at 23°C, Componenet B) | 1.01 | g/cm³ | — |
| Dynamic Viscosity (Component A, at 23°C, after stirring) | 15000 | mPa·s | ISO 3219 |
| Dynamic Viscosity (Component B, at 23°C, after stirring) | 800 | mPa·s | ISO 3219 |