Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Method
- Applications
- Automotive, Aerospace & Railway
- Formed-In-Place-Gaskets (Wet Type)
- Household Applications
- White Goods
- Application Details
Multipurpose grade for sealing and bonding in technical applications, e.g. CIPG- and FIPG-applications in automotive engines (oil pan, oil separator, valve covers).
Processing
- ELASTOSIL® N189 BLACK shows good primerless adhesion to many substrates. We recommend to run preliminary tests to optimize conditions for the particular application.
Properties
- Color
- Cured Properties
- Uncured Properties
- Properties
- Non-corrosive
- Coolant and oil resistant
- Excellent heat resistance up to 200°C, peak temperatures up to 220°C
- Electrically ablative
- Adhesion: Good adhesion to metals, glass and ceramics
- Crosslinking Property: One-component
- Product Rheology: Non-slump
- Resistance: Coolant resistant
- Resistance: Heat resistant
- Resistance: Oil resistant
- Note
- Curing conditions: 2 mm, 14 days storage at 23°C and 50% RH.
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.09 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Type 3, 23°C, 2mm) | 300 | % | ISO 37 |
| Shore Hardness A | 30 | — | DIN ISO 48-4 |
| Tensile Strength (Type 3, at 23°C, 2mm) | 1.7 | N/mm² | ISO 37 |
| Volume Resistivity (at 23°C) | 50 | Ohm-cm | IEC 62631-3-1 |
| Value | Units | Test Method / Conditions | |
| Density (at 23°C) | 1.07 | g/cm³ | DIN EN ISO 1183-1 A |
| Dynamic Viscosity (at 25°C, Shear rate 0.5 s⁻¹) | 900000 | mPa·s | DIN EN ISO 3219 |
| Dynamic Viscosity (at 25°C, Shear rate 25 s⁻¹) | 100000 | mPa·s | DIN EN ISO 3219 |
| Extrusion Mass Flow Rate (3.1 mm nozzle, 0.21 N/mm² pressure) | 11 | g/10s | Internal method |
| Skin Formating Time (at 23°C, 50% r.h) | 15 | minutes | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety Note
- During vulcanization of ELASTOSIL® N189 BLACK, a total of 4% by weight of an oxime is being split off. These vapors should not be inhaled for long periods or in high concentration. Work areas should therefore be well ventilated.
- Contact of unvulcanized silicone rubber with eyes and mucous membranes must be avoided as this would cause irritation. However if it does happen, rinse the affected area thoroughly with water.
Packaging & Availability
- Country Availability
- Regional Availability