Processing
Temperature Curing time, thickness 1 cm
100°C 240 min 130°C 40 min 150°C 10 min
Properties
- Physical Form
- Cured Properties
- Uncured Properties
- Properties
- One-part, ready-to-use
- Thixotropic (shear thinning)
- Rapid heat cure
- Forms a soft gel on vulcanization
- Low content of volatiles
- Low content of uncured polymer
- Low ion content
- Ultraviolett fluorescing
- Note
Cured for 30 min at 150°C.
Value | Units | Test Method / Conditions | |
Content Extractable Ion (Na, K, Li, Cl, at 121°C, 48 hours) | max. 5.0 | ppm | — |
Density (at 23°C) | 0.98 | g/cm³ | ISO 2781 |
Hardness Penetration (quarter cone, 9.38 g) | 5 | mm | DIN ISO 2137 |
Value | Units | Test Method / Conditions | |
Density (at 23°C) | 0.98 | g/cm³ | — |
Viscosity (at 25°C, Shear rate 0.5 s⁻¹) | 20000 | mPa·s | ISO 3219 |
Viscosity (at 25°C, Shear rate 100 s⁻¹) | 2500 | mPa·s | ISO 3219 |