Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
Features & Benefits
- Materials Features
- Ready-to-Use Product Features
- Special Features
- Addition Curing
- Excellent mechanical properties
- Flowable
- Two-component
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Applications
- Electrics & Electronics
- Reproduction Molding
- Application Details
- Encapsulation of electrical and electronic components.
- Coatings
- Manufacture of technical moldings by casting.
- Mold making
Processing
The platinum catalyst is contained in component B.
Caution
Only components A and B that have the same lot number may be processed together. To ensure optimum flow of the material, the components must be stirred thoroughly before they are removed or processed in their containers.
Pigmentation
If so desired, 1-4 wt % ELASTOSIL® Pigment Pastes FL can be added, preferably to Component A.
Properties
- Color
- Catalyst Properties
- Cured Properties
- Uncured Properties
- Properties
- Easy to process because of low viscosity
- Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat.
- Cures in closed systems
- Low Shore A hardness
- High elongation, outstanding tensile strength
- Excellent tear strength
- Cured rubber is translucent and colorless.
- Can be pigmented with 1-4 % ELASTOSIL® Pigment Pastes FL.
- Note
Compression molded 10 min at 100 °C for cured properties.
Value | Units | Test Method / Conditions | |
Curing Time (non-adhesive) | 12 | hours | — |
Dynamic Viscosity (at 23°C) | 12000 | mPa·s | ISO 3219 |
Mix Ratio (A:B) | 9:1 | parts by weight | — |
Pot Life (at 23°C, up to 100000 mPa.s) | 60 | minutes | — |
Value | Units | Test Method / Conditions | |
Density (in water, at 23°C) | 1.1 | g/cm³ | DIN EN ISO 1183-1 A |
Elongation (at break) | 600 | % | ISO 37 Type 1 |
Linear Shrinkage | max. 0.1 | % | — |
Shore Hardness A | 25 | — | DIN ISO 48-4 |
Tear Strength | 30 | N/mm | ASTM D 624 B |
Tensile Strength | 6.5 | N/mm² | ISO 37 Type 1 |
Value | Units | Test Method / Conditions | |
Density (at 23°C, Componenet A) | 1.1 | g/cm³ | DIN EN ISO 2811-1 |
Density (at 23°C, Componenet B) | 0.98 | g/cm³ | DIN EN ISO 2811-1 |
Dynamic Viscosity (Component A, at 23°C, after stirring) | 25000 | mPa·s | ISO 3219 |
Dynamic Viscosity (Component B, at 23°C, after stirring) | 900 | mPa·s | ISO 3219 |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety Note
Components A and B of the addition-curing grade ELASTOSIL® RT 625 A/B contain only constituents that over many years have proved to be neither toxic nor aggressive. Special handling precautions are therefore not required, i.e., only the general industrial hygiene regulations apply.
Packaging & Availability
- Country Availability
- Regional Availability